fiberglass bodies

[Goodesta]

does any1 have a how to?

advantages?


disadvantages?

 

[Larsenracing]

Fiberglass would be cool but would be much heavier than the lexan bodys as it would have to be thicker. Also the fiberglass that you would make to mold a body with would crack easily. If you could make it from a G10 Fiberglass that body would be awsome and basicly bulletproof but almost impossable to make. The g10 fiberglass I'm refering to is that same as what the Losi Slider chassis is made from.

 

[HopIt]

I bought a used T Maxx with a fiberglass hummer shell. It had seen some action but still looked OK until I tried to handle it. That stuff really gets into your skin. I would not use it for that reason, JMO.